بيانات تقنية سيراميك الزركونيا
|
ITEM |
UNIT |
Zro2 |
ZTA |
|
Density |
G/cm3 |
6.05 |
413 |
|
Bending Resistance |
Mpa |
1300 |
1000 |
|
Compressive Strength |
Mpa |
3000 |
3300 |
|
Elasticity Modulus |
Gpa |
205 |
320 |
|
Shock Strength |
Mpam/2 |
12 |
10 |
|
Vaporization Coefficient |
M |
25 |
20 |
|
Vickers Hardness |
HV0.5 |
1200 |
1700 |
|
Thermal Expansivity |
10-6K-1 |
10 |
9 |
|
Conductivity |
W/MK |
2 |
20 |
|
Thermal Shock Resistance |
AT℃ |
280 |
260 |
|
Maximum Service Temperature |
℃ |
1200 |
1600 |
|
20℃ Volume Resistance |
Ω |
≥1010 |
≥1012 |
|
Dielectric Strength |
KV/mm |
- |
- |
|
Apparent Porosity |
％ |
0 |
0 |
|
Permittivity |
Er |
- |
- |
|
Dielectric Loss Angle |
tanδ |
- |
- |
بيانات تكنولوجيا مسحوق الزركونيا
|
Check Items |
Results |
|
Composition |
ZrO2(HFO2)/Y2O3=94.48/5.22wt％ |
|
Al2O3 Conten |
0.25％ |
|
SiO2 Conten |
18.12ppm |
|
Fe2O3 Conten |
31.16ppm |
|
Na2O Conten |
8.1ppm |
|
Cl-Conten |
48.37ppm |
|
Surface Area |
7.38m2/g |
|
Original Particle Size |
32nm |
|
Size Distribution |
224nm |
|
Igition Loss |
3.17％(1100℃) |
|
Apparent Density |
1.24g/cm3 |
على وشك أن
قائمة المنتجات
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.
Fill in more information so that we can get in touch with you faster
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.
الآن الاتصال